FX-0171112
Design by Antonio Di Gennaro

Spear Tech Knives

FX-0171112

Blade Steel: N690Co stainless steel

Hardness: HRC 58-60

Blade Coating: Physical Vapor Deposition Gun Met

Handle: G10 black

Blade Length: 15 cm - 5.91"

Overall Length: 28 cm - 11.02"

Blade Thickness: 6 mm - 0.24"

Weight: 305 gr - 10.76 oz

  • Designer
    Antonio Di Gennaro
    “Before making any project, I try to understand the utility of the knife. Then I proceed with the design, trying to bring out my professional experience”.

    View all products designed by Antonio Di Gennaro

    view

    Antonio Di Gennaro
  • Blade
    Blade Coating: Physical Vapor Deposition Gun Met

    (Physical Vapor Deposition) is a variety of vacuum deposition methods used to deposit thin films by the condensation of a vaporized form of the desired film material onto various workpiece surface. The coating method involves purely physical process such as high temperature vacuum evaporation with subsequent condensation.

    Blade Steel: N690Co stainless steel

    Acciaio Steel Carbonio Carbon Cromo Chromium Cobalto Cobalt Azoto Nitrogen Manganese Manganese Molibdeno Molybdenu Nichel Nickel Fosforo Phosphorous Silicio Silicon Zolfo Sulfur Tungsteno Tungs Vanadio Vanadium
    N690CO 1.08 17.30 1.50 - 0.40 1.10 - - 0.40 - - 0.10

  • Gallery

Designer

Antonio Di Gennaro

“Before making any project, I try to understand the utility of the knife. Then I proceed with the design, trying to bring out my professional experience”.

View all products designed by Antonio Di Gennaro

view

Antonio Di Gennaro
Blade Coating: Physical Vapor Deposition Gun Met
(Physical Vapor Deposition) is a variety of vacuum deposition methods used to deposit thin films by the condensation of a vaporized form of the desired film material onto various workpiece surface. The coating method involves purely physical process such as high temperature vacuum evaporation with subsequent condensation.
Blade Steel: N690Co stainless steel
Acciaio Steel Carbonio Carbon Cromo Chromium Cobalto Cobalt Azoto Nitrogen Manganese Manganese Molibdeno Molybdenu Nichel Nickel Fosforo Phosphorous Silicio Silicon Zolfo Sulfur Tungsteno Tungs Vanadio Vanadium
N690CO 1.08 17.30 1.50 - 0.40 1.10 - - 0.40 - - 0.10